TI2 Flexible PVC Granules for Cable and Wire Sheathing Insulation

• Material: Polyvinyl Chloride/PVC
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Black
• Transport Package: 1000kg Jumbo Bag
• Model NO.: PVC Granules Compounds
• Specification: 70deg lead free PVC compound
• Trademark: longtai/jiangxi Anan
• Origin: China
• HS Code: 39042200
• Production Capacity: 1000tons/Month

Product Description

1.Technical specifications of 70 ºC pvc compound
 

Tensile strength	MPa	20.5
Fracture tensile strain	%	320
Ageing temperature	ºC	100
Ageing time	h	168
Tensile strength after ageing	MPa	22.5
Max change of tensile strength	%	+12
After ageing fracture tensile strain	%	290
Max change of fracture tensile strain	%	-10
Thermal deformation	%	28
Thermal ageing quality loss	g/m2	19
200ºC thermal stability time	min	90
20ºC volume resistivity	Ω.cm	2.0*1011

 
 
 
Technical specifications of  90 ºC pvc resin compound
 

Tensile strength	MPa	20
Fracture tensile strain	%	330
Ageing temperature	ºC	100
Ageing time	h	240
Tensile strength after ageing	MPa	21.5
Max change of tensile strength	%	+8
After ageing fracture tensile strain	%	310
Max change of fracture tensile strain	%	-6
Thermal deformation	%	28
Thermal ageing quality loss	g/m2	9
200ºC thermal stability time	min	120
20ºC volume resistivity	Ω.cm	2.0*1010

 
2,Use and standard: wire and cable
 
3,Process: extrusion
 
4,Appearance: cylindrical particles,  plastication should be good, the color and luster is even, without obvious impurity.
 
5,color: Any colors, base on requirement.
 
6,Packing: 25kg net weight or 1000kgs per jumbo bag



 
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
 
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting  compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.